I-PVB Resin ye-PVB Interlayer kunye nezinye izicelo
Umfanekiso weMveliso
| Izicelo | Ibanga | Uvavanyo lobutyheli | Iguquguqukayo into umxholo (%) | I-Hydroxyl umxholo (%) | Iqela le-Acetal Umxholo (%) | Umphunga | Ukuhanjiswa kokukhanya | Isalathisi sokunyibilika @120℃ (g/10min) | I-asidi yasimahla Umxholo (%) | Ukuxinana (isisombululo se-PVB se-10.0%) mPa.s | Unizi lolwapho kuyiwa khona (g/100mL) |
| I-PVB Interlayer | I-DVB201 | Akukho tyheli ebonakalayo | ≦ 1.5 | 17.0～20.0 | 75-80 | ≤0.40 | ≥87.0 | 0.90 -1.70 | ≤0.0100 | 1000～1400 | ≥ 14.0 |
| I-DVB202 | Akukho tyheli ebonakalayo | ≦ 1.5 | 17.0～20.0 | 75-80 | ≤0.40 | ≥87.0 | 1.30 -2.10 | ≤0.0100 | 900～1300 | ≥ 14.0 | |
| I-ceramic ye-elektroniki, i-coating, i-inki | Ibanga | Iguquguqukayo into umxholo (%) | I-Butyl i-aldehyde umxholo (wt%) | I-Hydroxyl umxholo (wt%) | I-asidi yasimahla Umxholo (%) | Ukuqaqamba 23℃（mPa.s） | |||||
| I-DVB402 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦0.50 | 10 ~ 30 | ||||||
| I-DVB412 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦0.50 | 30 ~ 50 | ||||||
| I-DVB413 | ≦ 3.0 | 71.0 ~74.0 | 24.0 ~ 27.0 | ≦0.50 | 10 ~ 60 | ||||||
| I-DVB422 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦0.50 | 50 ~ 80 | ||||||
| I-DVB432 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦0.50 | 100 ~ 170 | ||||||
| I-DVB433 | ≦ 3.0 | 71.0 ~74.0 | 24.0 ~ 27.0 | ≦0.50 | 140 ~ 220 | ||||||
| I-DVB462 | ≦ 3.0 | 76.0 ~ 80.0 | 18.0 ~ 21.0 | ≦0.50 | 40~ 90* | ||||||
| I-DVB463 | ≦ 3.0 | 71.0 ~74.0 | 24.0 ~ 27.0 | ≦0.50 | 60~ 120* | ||||||
*kwi-5%isisombululo se-ethanol, abanye bakwi-10%isisombululo se-ethanol